Unusual Hydrogen Explosions Due to Unexpected Metal-Water Reactions
- Type: Conference Presentation
- Conference Type: AIChE Spring Meeting and Global Congress on Process Safety
- Presentation Date: April 21, 2021
- Duration: 20 minutes
- Skill Level: Intermediate
- PDHs: 0.50
The first set of incidents are explosions due to inadvertent hydrogen generation from reactions of water with unprocessed incinerator bottom ash. A prime example is the December 2017 incident on a dry cargo ship carrying 2,333 metric tons of unprocessed incinerator bottom ash. The ash contained 2.6 % nonferrous metals including aluminum. The source of the water in the cargo hold was heavy rain during cargo loading. Laboratory tests with some cargo samples showed low rates of hydrogen generation per unit mass, but these generation rates in the unvented cargo hold were sufficient to develop a flammable atmosphere in the hold and in an adjacent ship store. The first explosion in the ship store was likely ignited by a spark in an actuated circuit braker. The second explosion, in the cargo hold, was more energetic and dislodged all the heavy steel secured hatch covers. There was one injury requiring hospitalization. An investigation uncovered reports of several land other explosion incidents involving water reactions with incinerator bottom ash.
The second type of metal-water reaction involves corroded copper cable in a moist atmosphere. One such incident occurred on a Rhode Island beach in which the beach sand covered an abandoned cable partially immersed in sea water. Samples of the sand revealed unusually high hydrogen concentrations. When the hydrogen-air mixture that formed above the hidden cable was somehow ignited, the resulting explosion caused a nearby woman to suffer broken ribs and other bruises. Subsequent to this incident, there have been accounts of other abandoned electrical cable under coastal beaches.
The third set of incidents entails zinc-water reactions in galvanized steel sprinkler system piping. A recent example is the explosion that occurred in a small sprinkler room during maintenance that entailed draining the pipe. The worker in the room suffered burn injuries and the building had to be evacuated. Subsequent investigation confirmed the zinc-water reaction mechanism and revealed that several other incidents have occurred in Scandanavian sprinkler systems that often have galvanized piping. Over time, the zinc layer in this piping will deteriorate due to zinc hydroxide formation and hydrogen accumulation. In some incidents the hydrogen accumulation levels caused sufficiently high pressures to result in pipe bursts.
The author hopes that the detailed accounts of these incidents and their investigations will allow the AIChE community to be more aware of inadvertent hydrogen generation scenarios in seemingly innocuous circumstances.