(369a) Synthesis and Steric Stabilization of Magnetite Nanoparticles with Triblock Copolymers

Davis, R. M., Virginia Polytechnic Institute and State University
Zhang, Q., Virginia Tech
Riffle, J., Virginia Tech

Magnetic nanoparticles are of great interest in developing new drug delivery systems and in medical diagnostic tests. The stabilization of nanoparticles of magnetite coated with a biocompatible polymer is of particular interest. The adsorption of novel triblock copolymers with end blocks comprised of copolymers of ethylene oxide (EO) and propylene oxide (PO) and a carboxylic acid/urethane center block was studied on particles of magnetite, Fe3O4 approximately 10 nm in diameter in aqueous media. Adsorption occurred via the carboxylic acid-containing center block and led to the formation of a brush layer that sterically stabilized the particles. The extension of the brush layer from the particle surface was modeled using mean field theory and the resulting steric contribution to the modified DLVO theory was sufficient to stabilize the particles in aqueous buffer for periods of weeks. Particle size with the adsorbed triblock stabilizer was measured by dynamic light scattering and by electron microscopy. The particle surface area was measured by the BET method and the amount of bound polymer was measured by thermal gravimetric analysis. The zeta potential was measured with an electrophoretic dynamic light scattering instrument. The effect of an external magnetic field on the colloid stability of the particles was also accounted for in the DLVO theory. The triblock copolymer composition was varied and the resulting effect on particle stabilization will be discussed.