(471d) Photoanode Area Dependent Efficiency and Recombination In Dye Sensitized Solar Cells | AIChE

(471d) Photoanode Area Dependent Efficiency and Recombination In Dye Sensitized Solar Cells

Authors 

Absher, J. - Presenter, University of Kentucky
Ellis, S. - Presenter, Conn Center for Renewable Energy Research


Current-voltage characterization was carried out on dye sensitized solar cells (DSSCs) with different photoanode areas ranging from 0.01 cm2 to 1 cm2. Surprisingly, we found that the short-circuit current density and the efficiency of the solar cells increased exponentially as the photoaonode area was reduced below 0.1 cm2. Furthermore, the fill factor remained constant in range of areas investigated and so this behaviour cannot be attributed to the resisitve losses in the solar cell. Understanding the electron transport and recombination in DSSCs with different photoanode areas could hold the key to explain these interesting results.

Several fundamental studies in literature have focused on understanding the electron transport and recombination in nanostructured photoanodes of DSSCs as the film thickness is altered. However, there have not been any reports which investigated how the transport and recombination and efficiency would be affected as the photoanode area of DSSCs varied. Only a few recent studies on organic solar cells have been reported where efficiency of the solar cells was found to dependent on the solar cell area.[1,2]  This motivated us to explore how electron transport, recombination are affected with a change in the photoanode area of the DSSC. Interestingly, we found that the transport time constants for these  cells of different areas remained the same, but the electron lifetimes increased as the photoanode area was reduced below 0.1 cm2. In addition, all these studies were performed with photoanodes comprising of different materials such as titania nanoparticles, tin oxide nanowires and tin oxide nanowire and titania nanoparticle composites and an increase in efficiency, short circuit current density and electron lifetime with a decrease in the cell area below 0.1 cm2 is observed in DSSCs  constructed with all these materials. Our results suggest the possibility of different recombination mechanism when the area of the solar cell is reduced below 0.1 cm2  and also points out the need for a standardized area for characterizing the performance of DSSCs.

[1] Gupta, D., Bag, M., Narayan S. Area dependent efficiency of organic solar cells. Applied Physics Letters 2008, 93, 163301-163304.

[2] Manor, E., Katz, E.A., Tromholt, T., Hirsch, B., Krebs, F.C. Orgin of size effect on the efficiency of organic photovoltaics. Journal of Applied physics 2011, 109, 074508-074517.