We are aware of an issue with certificate availability and are working diligently with the vendor to resolve. The vendor has indicated that, while users are unable to directly access their certificates, results are still being stored. Certificates will be available once the issue is resolved. Thank you for your patience.

(611b) Exponential Growth of Lbl Films with Incorporated Inorganic Sheets

Authors: 
Podsiadlo, P., University of Michigan
Michel, M., University of Michigan
Lee, J., University of Michigan
Verploegen, E., Massachusetts Institute of Technology
Wong Shi Kam, N., University of Michigan
Lee, J., University of Michigan
Ball, V., Institut National de la Santé et de la Recherche Médicale
Qi, Y., University of Michigan
Hart, A. J., Massachusetts Institute of Technology
Hammond, P. T., Massachusetts Institute of Technology
Kotov, N. A., University of Michigan


The fastest growth pattern of layer-by-layer (LBL) assembled films is exponential LBL (e-LBL), which has both fundamental and practical importance. It is associated with ?in-and-out? diffusion of flexible polymers, and thus was considered to be impossible for films containing clay sheets with strong barrier function, preventing diffusion. Here, we demonstrate that e-LBL for inorganic sheets is possible in a complex tri-component film of poly(ethyleneimine) (PEI), poly(acrylic acid) (PAA), and Na+-montmorillonite (MTM). This system displayed clear e-LBL patterns both in terms of initial accumulation of materials and unusually thick individual bilayers later in deposition process with film thicknesses reaching 200 ìm for films composed of 200 pairs of layers. Successful incorporation of MTM layers was observed by scanning electron microscopy and thermo-gravimetric analysis. Surprisingly, the growth rate was found to be nearly identical in films with and without clay layers, which suggests fast permeation/reptation of polyelectrolytes between the nanosheets during the ?in-and-out? diffusion of polymer. Considering these findings, e-LBL growth property is expected for a wide array of available inorganic nanoscale components and have a potential to greatly expand the e-LBL field and LBL field altogether. The large thickness and rapid growth of the films affords fast preparation of nanostructured materials which is essential for multiple practical applications ranging from optical devices to ultrastrong composites.