Short- and Long-Term Thermal Stabilities Of Imidazolium-Type Ionic Liquids On Catalytic Metal-Oxide Supports

Innovations of Green Process Engineering for Sustainable Energy and Environment
AIChE Annual Meeting
November 6, 2013 - 1:36pm-1:58pm
Ionic liquids (ILs) have been attracting tremendous attention in the last few decades because of their unique physicochemical properties , such as negligible vapor pressure , high thermal stability , high solvating capacity , and wide ranges of density and viscosity. With these tunable characteristics , they have become the first choice in many applications such as organic synthesis , electrochemistry , separation , and especially in catalysis.

In catalysis field , two directions of IL application recently discussed in the literature are particularly attractive: supported ionic liquid phase (SILP) catalysts and solid catalysts with ionic liquid layer(SCILL). Here , the utilization of ILs in these catalysts not only provides opportunities to control and stabilize the nuclearity and morphology of the active sites , but also offers the following opportunities to improve the catalytic performance: i) ILs can impose a positive influence on the “chemical” properties of the catalysts by acting as a co-catalyst , either as an acidic function in a bifunctional catalyst or as a modifier; ii) ILs can control the effective concentration of reaction intermediates and stabilize charged transition states or ligands to control the reaction pathways. SILP type catalysts , where active species dissolved in IL , act as a homogeneous system immobilized on a high surface area porous solid support offering the benefits of heterogeneous systems. Since support enables a higher surface area and IL enables the better utilization of catalyst particles in the pores , the system results in the higher selectivity and activity compared to traditional catalysts. Similar to the SILP catalyst concept in SCILL applications , a supported metal catalyst is coated with IL layer.

Although SILP and SCILL concepts offer improved activity and selectivity , applications of these IL-assisted supported catalysts are limited with the thermal stabilities of ILs. Thermal stability limits determined for pure ILs are not applicable for these systems. Because , ILs directly interact with the metal-oxide supports and these interactions influence the thermal stability of ILs significantly. Therefore , elucidation of structural factors determining the thermal stability limits of ILs on metal-oxide supports is crucial for the selection of optimum IL for the application conditions of IL-assisted supported catalysts. Here we report the short-term and long-term thermal stability limits of 34 different imidazolium-based ILs coated on commonly used metal-oxide supports , SiO2 , γ-Al2O3 , MgO. Structures of imidazolium ILs were varied systematically and the acidity of the support material increased from MgO to γ-Al2O3 and to SiO2.

Short-term thermal decomposition temperatures of ILs supported on metal-oxides were determined by thermogravimetric analysis (TGA) at a linear heating rate of 10K/min from 298 to 1073 K from the onsets of the derivative per cent weight changes. Results show that thermal stability of pure ILs significantly changes upon coating on metal-oxides with different point of zero charges (PZC) such as < 2.82 for SiO2 , 6-9.3 for γ-Al2O3 and 11.6-12 for MgO. Pure 1-ethyl-3-methylimidazolium tetrafluoroborate [EMIM][BF4] , for example , is reported to be stable up to 723 K; however , our data illustrate that it starts to decompose at 609 ± 3 , 534 ± 3 and 446 ± 3  K when coated on SiO2 , γ-Al2O3 , andMgO , respectively.  In general , imidazolium type ILs lose their thermal stability significantly as the acidity of the support decreases from SiO2 to MgO.  However , ILs with high acidity levels such as those with dicyanamide [DCA]- anion , 1 ,3-dimethoxyimidazolium bis(trifluoromethylsulfonyl)imide [DMOIM][NTf2] and 1 ,3-dihydroxyimidazolium bis(trifluoromethylsulfonyl)imide [DHIM][NTf2] and 1-ethyl-3-methylimidazolium hexafluorophosphate [EMIM][PF6] do not follow this general trend and show higher thermal stabilities on MgO than on SiO2.  Similarly , effects of increase in the length of alkyl groups attached to the imidazolium ring depend strongly on the anion type too.  For instance , thermal decomposition temperatures of [EMIM][BF4] , 1-butyl-3-methylimidazolium tetrafluoroborate [BMIM][BF4] , 1-hexyl-3-methylimidazolium tetrafluoroborate [HMIM][BF4] and 1-decyl-3-methylimidazolium tetrafluoroborate [C10MIM][BF4] were determined on the SiO2 , γ-Al2O3 , MgO metal-oxide supports. Results show that thermal stabilities of these ILs decrease from 609 ± 3 to 502 ± 3 K on SiO2 , from 534 ± 3 to 496 ± 3 K on γ-Al2O3 and from 446 ± 3 to 440 ± 3 K upon step-wise increase in the length of alkyl chain attached to the imidazolium ring from ethyl to decyl. However , when [BF4]- anion is replaced with [NTf2]- , increase in the alkyl chain length of cation does not affect the thermal stability significantly.  Similarly when the butyl chain was replaced with a nucleophilic cyanopropyl group on imidazolium ring with [NTf2]-anion , data does not indicate any effect on the thermal decomposition temperature on the same support.

As shown in Figure 1 , thermal stabilities of ILs with [BMIM]+ cation on various metal-oxides vary linearly with the chemical shift value of acidic (C2)-H on imidazolium ring. Moreover , slopes of these lines depend strongly on the PZCs of the metal-oxide supports. Thus , we infer that there is a strong correlation between the thermal stabilities of ILs with their acidity levels and the PZCs of supports.

In order to complement the TGA-based short-term thermal stability results , long-term thermal stability limits of ILs on metal-oxides were also investigated.  For this purpose , ILs on various metal oxides were characterized by FTIR spectroscopy and SEM analysis with EDX mapping before and after 6 hour-long isothermal treatments at various temperatures. Results illustrated that some ILs start to decompose earlier than the temperatures determined by quick TGA scans while others remain intact up to the TGA-determined decomposition temperatures. As an example , on γ-Al2O3 metal-oxide support , [EMIM][BF4] is stable up to the 534 ± 3 K (temperature determined with TGA scans) while [C10MIM][BF4] starts to decompose after 473 ± 3 K , earlier than the TGA-determined temperature.

In summary , results presented here provide the basis for selecting stable ILs for IL-assisted supported-catalysts based on their application conditions.

Professional Development Hours
0.5 PDHs
You will be able to download and print a certificate for these PDH credits once the content has been viewed. If you have already viewed this content, please click here to login.
Presenter(s): 

Would you like to access this content?

No problem. You just have to complete the following steps.

You have completed 0 of 2 steps.

  1. Log in

    You must be logged in to view this content. Log in now.

  2. Purchase Technical Presentation

    You must purchase this technical presentation using one of the options below.
    If you already purchased this content recently, please click here to refresh the system's record of ownerships.

Pricing

Credits 0.5 Use credits
List Price $25.00 Buy now
AIChE Members $15.00 Buy now
AIChE Undergraduate Student Members Free Free access
AIChE Graduate Student Members Free Free access
Related Topics: 
Skill Level: